KJ3242X1-BK1防水透气材料的原理Principle of waterproof and breathable materialsGeneral waterproof and breathable materials are composed of polymer waterproof and breathable film and flame retardant cloth. There are tiny pores in the polymer waterproof and breathable film, and the diameter of the pores is a few tenths to dozens μ m。 The average value of rainwater droplet diameter is shown in Table 1. From Table 1, it can be seen that the pore diameter of the polymer waterproof film is much smaller than the diameter of the water drop, or even less than one thousandth of the diameter of the water drop. Therefore, at normal temperature, when water exists in liquid form, it is impossible to enter the sensor through the waterproof and breathable material, while the diameter of the air molecule is much smaller than the pore diameter of the waterproof and breathable material, and it can be penetrated. Based on this, this material can achieve the purpose of waterproof and breathable. 1.3 Selection of waterproof and breathable materials

一般的防水透气材料由高分子防水透气薄膜和阻燃布复合而成。高分子防水透气薄膜内有微小的孔隙，孔的直径为零点几到几十μm。雨水水珠直径的平均值如表1所示。从表1 中看出，高分子防水薄膜的孔隙直径比水滴直径小很多，甚至不到水滴直径的千分，所以在常温状态下，水以液态形式存在时，是不可能通过防水透气材料进入传感器内部的，而空气分子的直径比防水透气材料的孔隙直径小很多，可以透过，基于此该种材料就能达到防水透气的目的。1.3 防水透气材料的选择

防水透气材料主要分为以下四大类：高密织物、层压织物、涂层织物和膨化织物。

本文探讨的传感器用防水透气材料是由聚四氟乙烯薄膜膨化拉伸扩展而成的，被拉伸的聚四氟乙烯膜在三维方向均形成了网状结构。优异拉伸技术能够使微孔直径保持在0.3 ～ 1.2 μm，远远小于水珠直径，阻水性能优异，*小轻雾也不能通过；同时微孔直径又远大于气体分子；所以该种材料具备防水功能的同时，也能允许气体分子轻松通过；材料使用温度范围为（-55 ～ 200）℃，可满足大部分压力传感器的工作温度要求。

1.4 防水透气材料在表压传感器上的应用

1.4.1 传感器通气结构设计

传感器的结构设计针对表压传感器的密封防护和防水性的要求，综合各方面考虑在传感器外壳上端设计了安装防水透气组件的通气孔，以此来实现整个传感器的通气和防水功能。图3 为传感器通气结构示意图。

与防水透气组件对接的螺纹接口处使用密封圈密封，从而保证传感器与外界环境的连通，通过组件可以隔绝水分进入传感器内部，达到透气防水的目的。为了保证防水和防振动的效果，在螺纹处涂抹少量螺纹保护胶。1.4.2 防水透气组件设计

防水透气组件选择金属材料，通过螺纹连接方式安装到传感器的合适位置，同时应考虑工作温度、环境湿度、防水要求和冲击、振动等环境适应性要求。

防水透气组件内部为通孔设计，使得组件与外界环境相通，将聚四氟乙烯膨化材料填充在组件内部，四周压紧，防止水分从聚四氟乙烯膨化材料与组件安装面进入，组件采用螺纹机械接口，可以设计成M3/M4 等直径较小螺纹，为后续组件安装预留足够安装空间，组件如下图所示。2 实验验证